The urethane base material was immersed in a Ti slurry to adsorb Ti particles on the surface. After the urethane was removed by heat treatment at 600 °C, sintering at 1300 °C was performed, whereby the Ti particles were sintered and bonded. Using this process, a porous Ti body with a structure similar to the base urethane form was produced [11].